Alloy: 2A12
Temper:T4/T3
thickness: 0.3mm-4.0mm
width: 1000mm-2600mm
surface: mill finish or at request
standard: GB/T3880 、EN485、ASTM B209
Quantity: | |
---|---|
2A12 aluminum alloy is a kind of high-strength hard aluminum, which can be strengthened by heat treatment; 2A12 aluminum alloy has good spot weldability, and there is a tendency to form intergranular cracks when gas welding and argon arc welding. 2A12 aluminum alloy has good machinability after cold work hardening. Corrosion resistance is not high, often using anodic oxidation treatment and painting methods or adding aluminum coating on the surface to improve corrosion resistance.
SPECIFICATION
2A12 T4/T3 aluminum alloy plate:
Regular thickness range: 0.3-4mm
Regular width range: 1000-2600mm
The following table shows the chemical composition of aluminium / aluminum 2A12 alloy.
Chemical Composition
Si | Fe | Cu | Mn | Mg | Cr | Zn | Ti | Standard |
0.2-0.8 | 0.7 | 3.5-4.5 | 0.4-1.0 | 0.4-0.8 | 0.1 | 0.25 | 0.15 | GB/T3190 ASTM B209 EN573 |
The physical properties of aluminium / aluminum 2A12 alloy are outlined in the following table.
2A12 T4/T3 aluminum alloy plate mechanical properties:
Temper | Thickness/mm | Rm(Mpa) Tensile Strength | Rp0.2(MPa)Yield Strength | A50% Breaking Elongation | Standard | |||
Standard | zhuxia performance | Standard | zhuxia performance | Standard | zhuxia performance | |||
T4 | 0.3-3.5 | ≥405 | 4150-430 | ≥270 | 285-300 | ≥15 | 15-20 | GB/T3880 、EN485、ASTM B209 |
* Remarks: Specific requirement of alloy, temper or specification can be discussed at your request.