2A14 T6 Extruded Aluminum Bar Hexagonal Bar For Aerospace Use

Alloy: 2A14
Temper: T6
Diameter: 40mm-350mm
Standard: GB/T 3190

Quantity:


2A14 belongs to both hard aluminum alloy and wrought aluminum alloy in terms of composition. Compared with 2A50, due to the higher copper content, it has higher strength and better thermal strength, but its plasticity in hot state is not as good as 2A50. It has good machinability, good contact welding, spot welding and seam welding performance, poor arc welding and gas welding performance; heat treatment can be strengthened, with extrusion effect; corrosion resistance is not high, and there is a tendency for inter-inspection corrosion during artificial aging. Therefore, the longitudinal and transverse properties are different; the corrosion resistance is not high, but the tendency of intergranular corrosion and stress corrosion cracking in the artificial aging state.


SPECIFICATION


2A14 T6 aluminum alloy extruded bar:

Diameter:  40-350mm

Regular width range:  1200-3800mm


The following table shows the chemical composition of aluminium / aluminum 2A14 alloy.

Chemical Composition

SiFeCuMnMgCrZn
ZrTi
0.6-1.20.73.9-4.8 0.4-1.0 0.4-0.8/0.3//0.15


The physical properties of aluminium / aluminum 2A14 alloy are outlined in the following table.

2A14 T6 aluminum alloy extruded bars mechanical properties:

AlloyTemper

(mm)

Corse Grain

Zone Depth

(mm)

Diameter

Rm(Mpa)

Tensile Strength

Rp0.2(MPa)

Yield Strength

(%)

Elongation

Standard
2A14T6≤5>22-150450-10GB/T 3910


* Remarks: Specific requirement of alloy, temper or specification can be discussed at your request.


Related News

content is empty!

Products

Quick Links

Contact Us
  +86-028-87585792
   Joshua Ning
   +86-18820808108
  alnan.aluminium@outlook.com
Get In Touch

Contact us
© 2020 ZhuXia Metal Products Co., Ltd. All rights reserved. 
Technology by leadong