6016 aluminum is a 6000-series aluminum alloy: there is significant alloying with both magnesium and silicon, and the alloy is formulated for primary forming into wrought products. aluminum 6016 can have the highest ductility among the 6000-series alloys in the database.
6016 T4 aluminum is 6016 aluminum in the T4 temper. To achieve this temper, the metal is solution heat-treated and naturally aged. the degree of differential hardening is much larger for 6016 T4 than for O temper.
Specification
Alloy | Temper | Thickness(mm) | Width(mm) |
6016 | T4/T4P | 0.5-1.5 | 1200-2650 |
Mechanical Properties
Alloy | Temper | Yield Strength Rp0.2(Mpa) | Tensile Strength Rm(Mpa) | Elongation at Break A80% | Elongation Uniform Ag% | Plastic Strain Ratio r | Strain Hardening Exponent n | Yield Tensile ratio Rp/Rm |
6016 | T4/T4P | 85-130 | 205-240 | ≥24 | ≥20 | ≥0.6 | ≥0.26 | ≤0.55 |
Chemical Composition
Alloy | Si | Fe | Cu | Mn | Mg | Cr | Zn | Ti | Standard |
6016 | 1.0-1.5 | 0.50 | 0.20 | 0.20 | 0.25-0.6 | 0.10 | 0.20 | 0.15 |
|
Typical applications of 6016 T4:
Applied to the automotive hood, automotive door and automotive roof. (Coil)