Alloy: 7A04
Temper:T6
thickness: 0.55mm-4.0mm
width: 1000mm-2600mm
surface: mill finish or at request
standard: GB/T3880 、EN485、ASTM B209
| Quantity: | |
|---|---|
7A04 aluminum alloy is the most commonly used super-durable aluminum, a high-strength alloy that can be strengthened by heat treatment. 7A04 aluminum sheet is usually used under the condition of quenched artificial aging. At this time, the strength is much higher than that of general duralumin, but the plasticity is lower. Extruded semi-finished products and aluminum clad plates that are not too thick in cross section have good corrosion resistance and tend to have stress concentration. The spot weldability is good, the gas welding is poor, the machinability is good after the heat treatment, and the annealing state is low.
SPECIFICATION
7A04 T6 aluminum alloy plate:
Regular thickness range: 0.3-4mm
Regular width range: 1000-2600mm
The following table shows the chemical composition of aluminium / aluminum 7A04 alloy.
Chemical Composition
Si | Fe | Cu | Mn | Mg | Cr | Zn | Ti | Standard |
0.5 | 0.5 | 1.4-2.0 | 0.2-0.6 | 1.8-2.8 | 0.1-0.25 | 5.0-7.0 | 0.1 | GB/T3190 ASTM B209 EN573 |
The physical properties of aluminium / aluminum 7A04 alloy are outlined in the following table.
7A04 T6 aluminum alloy plate mechanical properties:
| Temper | Thickness/mm | Rm(Mpa) Tensile Strength | Rp0.2(MPa)Yield Strength | A50% Breaking Elongation | Standard | |||
| Standard | zhuxia performance | Standard | zhuxia performance | Standard | zhuxia performance | |||
| T6 | 0.5-3.5 | ≥480 | 565-595 | ≥400 | 495-510 | ≥7 | 10-14 | GB/T3880 、EN485、ASTM B209 |
* Remarks: Specific requirement of alloy, temper or specification can be discussed at your request.