Materials are the foundation of the aviation equipment manufacturing industry. Due to the special service conditions of aviation equipment, the aviation industry has extremely strict requirements for the selection of aviation equipment materials.
Among the aluminum alloy series, 7000 series high-strength aluminum alloys are widely used in the manufacture of parts for aviation equipment due to their light weight, high tensile strength and strong corrosion resistance. One of them, 7A85 aluminum alloy, as a new type of high-strength alloy developed by China, has attracted wide attention from aviation component manufacturers with its improved excellent performance.
7A85 aluminum alloy is a new type of aluminum alloy developed in China through microalloying and heat treatment. The alloy composition is equivalent to 7085 aluminum alloy, but due to the composition optimization and processing technology improvement, 7A85 aluminum alloy has higher fracture toughness and lower quenching sensitivity, and is more suitable for manufacturing aviation parts.
7A85 T7651/T7452 aluminum alloy plate:
Regular thickness range: 4-260mm
Regular width range: 1200-3800mm
The following table shows the chemical composition of aluminium / aluminum 7A85 alloy.
The physical properties of aluminium / aluminum 7A85 alloy are outlined in the following table.
7A85 T7651/T7452 aluminum alloy plate mechanical properties:
|Temper||Direction||Thickness/mm||Rm(Mpa) Tensile Strength||Rp0.2(MPa)Yield Strength||A50% Breaking Elongation||Standard|
|Standard||zhuxia performance||Standard||zhuxia performance||Standard||zhuxia performance|
* Remarks: Specific requirement of alloy, temper or specification can be discussed at your request.